CD3MWCuN (UNS J93380), is super duplex stainless steel, with greater corrosive resistance than standard SS2205, mainly used for service in high corrosive conditions. WwW.CASTINGQUALITY.COM
ASTM A351 Grade CD3MWCuN; ASTM A890 Grade 6A; ASTM A995 Grade 6A, Type 25Cr-7Ni-Mo-N; Casting UNS J933380; ACI CD3MWCuN;
Casting Methods in Casting Quality Industrial:
- Sand Casting
- Investment Casting (Lost Wax Casting, Precision Casting)
CD3MWCuN, 6A (UNS J93380) Equivalent Stainless Steel Grade:WwW.CASTINGQUALITY.COM
ASTM A789 /ASTM A790/ASTM A276: Wrought UNS S32760;
ASTM A182 F55
Reference Casting Standards and others:
ASTM A351 Standard Specification for Castings, Austenitic, for Pressure-Containing Parts.
ASTM A890/890M Standard Specification for Castings, Iron-Chromium-Nickel-Molybdenum Corrosion-Resistant, Duplex (Austenitic/Ferritic) for General Application.
ASTM A995/995M Standard Specification for Castings, Austenitic-Ferritic (Duplex) Stainless Steel, for Pressure-Containing Parts.

Our Services
- Sand Casting
- Investment Casting
- Shell Casting
- CNC Machining
- CAD Design
- Tools/Mold Design
Stainless Steel Grade | CD3MWCuN Chemical Composition / Physical Properties % (max, except where range is given) | ||||||||||||
Standard | Grade | ACI | Carbon | Manganese | Silicon | Sulfur | Phosphorus | Chromium | Nickel | Molybdenum | Nitrogen | Copper | Tungsten |
ASTM A351 | CD3MWCuN | – | 0.03 | 1.00 | 1.00 | 0.025 | 0.030 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.20-0.30 | 0.5-1.0 | 0.5-1.0 |
ASTM A890 | 6A | CD3MWCuN | 0.03 | 1.00 | 1.00 | 0.025 | 0.030 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.20-0.30 | 0.5-1.0 | 0.5-1.0 |
ASTM A995 | 6A | CD3MWCuN | 0.03 | 1.00 | 1.00 | 0.025 | 0.030 | 24.0-26.0 | 6.5-8.5 | 3.0-4.0 | 0.20-0.30 | 0.5-1.0 | 0.5-1.0 |
%Cr+3.3%Mo+16%N>=40 |
CD3MWCuN Heat treatment process: WWW.CASTINGQUALITY.COM
Heat to 2010°F [1100°C] minimum, hold for sufficient time to heat casting uniformly to temperature, quench in water or rapid cool by other means.
CD3MWCuN Stainless Steel Mechanical Property: WWW.CASTINGQUALITY.COM
Stainless Steel Grade | Tensile Strength min | Yield Strength, min | Elongation, min | |||||
Standard | Grade | ACI | UNS | Ksi | MPa | Ksi | MPa | % |
ASTM A351 | CD3MWCuN | – | J93380 | 100 | 700 | 65 | 450 | 25 |
ASTM A890 | 6A | CD3MWCuN | J93380 | 100 | 690 | 65 | 450 | 25 |
ASTM A995 | 6A | CD3MWCuN | J93380 | 100 | 690 | 65 | 450 | 25 |
CD3MWCuN compared with other similar stainless steel grades: WWW.CASTINGQUALITY.COM
Steel Grade | C | Mn | P | S | Si | Ni | Cr | Mo | N | Cu | W | |
A182 F55 | S32760 | 0.03 | 1.00 | 0.030 | 0.010 | 1.00 | 6.0-8.0 | 24.0-26.0 | 3.0-4.0 | 0.20-0.30 | 0.50-1.00 | 0.50-1.00 |
A790 A789 | S32760 | 0.05 | 1.00 | 0.030 | 0.010 | 1.00 | 6.0-8.0 | 24.0-26.0 | 3.0-4.0 | 0.20-0.30 | 0.50-1.00 | 0.50-1.00 |
A479 | S32760 | 0.03 | 1.00 | 0.030 | 0.010 | 1.00 | 6.0-8.0 | 24.0-26.0 | 3.0-4.0 | 0.20-0.30 | 0.50-1.00 | 0.50-1.00 |
Steel Grade | Tensile | Yield | Elongation | Reduction | Hardness | |||||||
A182 F53 | S32760 | 109-130Ksi(750-895Mpa) | 80Ksi (550Mpa) | 25% | 45% | |||||||
A790 A789 | S32760 | 109-130Ksi(750-895Mpa) | 80Ksi (550Mpa) | 25% | – | 270HB | ||||||
A479 | S32760 | 109Ksi(750Mpa) | 80Ksi (550Mpa) | 25% | – | 300HB |
CD3MWCuN Typical Application
- Pump components casting
- Valve components casting
- Heat exchangers
- Offshore systems.
- Pressure vessels.
Can CD3MWCuN grade material be weld repaired ? Which electrode or filler wire to be used? Is there any procedure for weld repair like, preheat to hand touch temperature, welding in a controlled way to reduce the heat input.