Aluminum EN-AC-43400

EN-AC-43400 (EN AC-AL Si10Mg(Fe)) is one popular AL-SI alloy aluminum for die casting only

 

Reference Standard

DIN EN 1706:2013 Aluminium and aluminium alloys – Castings – Chemical composition and mechanical properties  

 

EN AC 43400, EN AC-AL Si10Mg(Fe) EquivalentMetal Grades

DIN 1725-2 Grade G-AlSi10Mg (DIN 3.2382)

GB/T 1173 Grade YZALSi10Mg (YL104)

ASTM E527 Grade A13600

ISO 3522 Grade AlSi10Mg(Fe)

JIS H5202 Grade ADC3

Casting Manufacture Process for EN-AC-43400 (EN AC-AL Si10Mg(Fe)):

  • Pressure Die Casting

 

EN-AC-43400 (EN AC-AL Si10Mg(Fe)) Chemical Requirement

StandardEN 1706
NumericalEN AC-43400
Chemical SymbolsEN AC – Al Si10Mg(Fe)
Si9.0-11.0
Fe max1.0

(0.45-0.9)

Cu max0.10

(0.08)

Mn max0.55
Mg0.20-0.50

(0.25-0.50)

Cr
Ni max0.15
Zn max0.15
Pb max0.15
Sn max0.05
Ti0.20

(0.15)

Others, each0.05
Others, total0.15
AluminumRemainder

Our Services

  1. Sand Casting
  2. Investment Casting
  3. Shell Casting
  4. CNC Machining
  5. CAD Design
  6. Tools/Mold Design

 

EN-AC-43400 (EN AC-AL Si10Mg(Fe)) Mechanical Property

StandardEN 1706EN 1706EN 1706EN 1706
NumericalEN AC-43400EN AC-43400EN AC-43400EN AC-43400
Chemical SymbolsEN AC-ALSi10Mg(Fe)EN AC-ALSi10Mg(Fe)EN AC-ALSi10Mg(Fe)EN AC-ALSi10Mg(Fe)
Separately Cast Test PiecesSand CastChill CastInvestment CastPressure Die Cast
Temper DesignationF
Tensile Strength  Rm

Mpa,min

240
Yield Strength Rp0.2

Mpa, min

140
Elongation, A

%, min

1
Hardness, HBW, min70

 

Heat Treatment Process for EN-AC-43400 (EN AC-AL Si10Mg)

NO NEED HEAT TREATMENT

F-CASTING

 

EN-AC-43400 (EN AC-AL Si10Mg) Application

Building Industry

Machinery Spare Parts

 

 

 

 

SERVICE IN QINGDAO CASTING QUALITY INDUSTIRAL

  • SAND CASTING
  • INVESTMENT CASTING
  • SHELL CASTING
  • PERMANENT MOLD CASTING
  • CNC MACHININING

Metal Castings

Aluminium , ,