Specifies requirements for the chemical compositions, mechanical properties and other characteristics for (a) Copper alloy ingots intended to be remelted for the production of castings. (b) Copper alloy and high conductivity copper castings
PDF VIEWOur Services
- Sand Casting
- Investment Casting
- Shell Casting
- CNC Machining
- CAD Design
- Tools/Mold Design
| Stainless Steel Grade | LCC Chemical Composition / Physical Properties % (max, except where range is given) | ||||||||||
| Standard | Grade | Carbon | Silicon | Manganese | Phosphorus | Sulfur | Nickel | Chromium | Molybdenum | Copper | Vanadium |
| ASTM A352 | LC1 | 0.25 | 0.60 | 0.50-0.80 | 0.04 | 0.045 | – | – | 0.45-0.65 | – | – |
| Element, % (max, except where range is given). | |||||||||||
ASTM A352 GR. LC1 Heat treatment process: www.castingquality.com
Ferrite castings shall be furnished in the normalized and tempered or liquid-quenched and tempered condition. Castings shall be tempered at a minimum of 1100°F [590°C], followed by cooling in air or liquid
Castings shall be allowed to cool below the transformation, range directly after pouring and solidification before they are reheated for normalizing or liquid quenching.
ASTM A352 GR. LC1 Stainless Steel Mechanical Property www.castingquality.com
| Stainless Steel Grade | Tensile Strength min | Yield Strength, min | Elongation, min | Reduction of Area, min | Impact Requirement Charpy V-Notch Ft-lbf [J] | ||||||
| Standard | Grade | UNS | Ksi | MPa | Ksi | MPa | % | % | Everage | Single | Temperature °F [°C] |
| ASTM A352 | LC1 | J12522 | 65.0-90.0 | 450-620 | 35.0 | 240 | 24 | 35 | 13[18] | 10[14] | -75 [-59] |
ASTM A352 GR. LC1 Typical Casting Application
- Pump Castings.
- Valve Castings.
- Water System castings.
- Low temperature condition.
- Heat Exchanger System.