LC1 is one Carbon Molybdenum casting grade which listed in ASTM A352/352M standard only. UNS code is J12522. It’s a popular grade for low temperature application.www.castingquality.com
Casting Methods in Casting Quality Industrial:
- Sand Casting
- Investment Casting (Lost Wax Casting, Precision Casting)
ASTM A352 LC1 Equivalent Steel Grade: www.castingquality.com
SCPH11, GS-22Mo4, FC1-M, 240B1
Reference Casting Standards:
ASTM A352 Standard Specification for Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service.
PDF VIEWOur Services
- Sand Casting
Casting Quality focus on Metal Parts industry, we provide professional service in Metal Casting field.
Sand Casting is a popular metal form method, are suitable for all materiel, such as grey iron, ductile iron, malleable iron, carbon steel, stainless steel, aluminum and bronze.
- Investment Casting
also named as precision lost wax casting, mainly suitalbe for carbon steel and stainless steel parts. We also provide grey iron and ductile iron and aluminum and bronze parts by investment casting. It can achieve the best appearance with good tolerance
- Shell Casting
Shell casting method is a good option to replace investment casting and sand casting. the quality is better than sand casting parts, suitable for bulk production.
- CNC Machining
CNC Milling, CNC turning with 5 xix CNC center, we provide precision machining for all castings based on customers design drawings.
- CAD Design
Mechanical Design service based on customers requirement, our software is Solidworks and AutoCAD.
- Tools/Mold Design
Mould design and production will be served for metal casting ad plastic injection industry. Based on our more than 10 years experience, we supply professional molds for our customers in Europe and North American.
| Stainless Steel Grade | LC1 Chemical Composition / Physical Properties % (max, except where range is given) | ||||||||||
| Standard | Grade | Carbon | Silicon | Manganese | Phosphorus | Sulfur | Nickel | Chromium | Molybdenum | Copper | Vanadium |
| ASTM A352 | LC1 | 0.25 | 0.60 | 0.50-0.80 | 0.04 | 0.045 | – | – | 0.45-0.65 | – | – |
| Element, % (max, except where range is given). | |||||||||||
ASTM A352 GR. LC1 Heat treatment process: www.castingquality.com
Ferrite castings shall be furnished in the normalized and tempered or liquid-quenched and tempered condition. Castings shall be tempered at a minimum of 1100°F [590°C], followed by cooling in air or liquid
Castings shall be allowed to cool below the transformation, range directly after pouring and solidification before they are reheated for normalizing or liquid quenching.
ASTM A352 GR. LC1 Stainless Steel Mechanical Property www.castingquality.com
| Stainless Steel Grade | Tensile Strength min | Yield Strength, min | Elongation, min | Reduction of Area, min | Impact Requirement Charpy V-Notch Ft-lbf [J] | ||||||
| Standard | Grade | UNS | Ksi | MPa | Ksi | MPa | % | % | Everage | Single | Temperature °F [°C] |
| ASTM A352 | LC1 | J12522 | 65.0-90.0 | 450-620 | 35.0 | 240 | 24 | 35 | 13[18] | 10[14] | -75 [-59] |
ASTM A352 GR. LC1 Typical Casting Application
- Pump Castings.
- Valve Castings.
- Water System castings.
- Low temperature condition.
- Heat Exchanger System.